ロッドティップから一つ目のスネークガイドを取り外してトップガイドを取り付けたJ. Bailey 7’0″ #4-#5のトップガイド下の部分に装飾用のナイロンスレッド（GUDEBROD A5274）を巻いて、Flex Coatでコーティングしました。

ロッド製作用ツールやコーティング剤、スレッドを収納した透明プラスチックケースをおよそ15年ぶりにクロゼットから取り出してみると、未使用のFlex Coatロッドラッピング用コーティング剤がありました。

シリンジ2本とミキシングカップ4個、筆4本と攪拌棒4本がセットになったキット製品です。取扱説明書にわかりやすい説明文が書いてあるので転記しておきます。重要と思われる箇所に下線を引きました。

DIRECTIONS

1. Visually study both syringes to become familiar with the graduated markings and to check for equal contents of the syringes. Have paper towels handy for clean up of any drips or spills. In cold weather, make sure finish is warmed prior to mixing for better results. See Helpful Tip #1. Support your rod horizontally. See Helpful Tip #9.

1. Dispense from syringes equal portions of resin A and hardener B into mixing cup included. 3cc of each part should finish an average rod.

1. Mix thoroughly with stir stick included. Mixture at first will become cloudy, then clear when thoroughly mixed.

1. While rotating the rod, use a brush to apply the Flex Coat mixture to the rod wraps. Extend the finish slightly over the ends of the wraps to completely protect them. Coat all wrappings quickly, working around the rod to apply the finish. Apply a little more finish than needed to allow the finish to soak in. If required, remove excess later when leveling the finish. Let stand a few minutes and then level out the finish with lengthwide brush strokes.

1. For even drying, rotate the rod ½ turns as needed to prevent sagging of the finish. Depending upon the thickness of the finish and the ambient temperature, rotate the rod from 15 minutes to 1½ hours. Flex Coat will set to touch in about 6 hours. A small slow gear motor (one to 30 rpm) can be used to continually turn the rod also. If desired, more than one coat may be applied without any surface preparation of previous coat.

混ぜ合わせた樹脂Aと硬化剤Bは、最初は白濁するが、念入りに混ぜると透明になるとあります。およそ20年前にTOHOの2液性エポキシコート剤を使用してグラファイトロッド数本のスレッドをコーティングしたことがありますが、その時はコーティング後に白濁が残り、苦労した記憶があります。Flex Coatの製品は白濁しないようです。

低速モーターも透明プラスチックケースに入ってました。使用するのはおよそ20年ぶりになります。コーティング剤は乾燥するまで垂れるので、この低速モーターを用いてロッドを回転させる必要があります。手動で回転させることも可能ですが、垂れなくなるまでずっと側にいなければなりません。バルセロナで開催されたF1スペインGP決勝をテレビ観戦していると、ちょうど1時間半ぐらいが経ち、コーティング剤が垂れなくなりました。周囲の気温や湿度にもよりますが、完全に乾燥するまでは6時間以上、要します。

巻いたスレッドに隙間があり、Flex Coatの厚みが均一ではありませんが、実用上、問題はありません。しかし、これでは美しくないので、完全に乾燥すれば、やり直そうと考えています。フライフィッシングは釣果ではなく、ロッドや毛鉤の製作、フィールドでのキャスティングなど過程こそが最も大事です。過程に満足できなければ、その過程をやり直して楽しむことができます。

Flex Coat取扱説明書に記載の役立つコツも以下に転記しておきます。

HELPFUL TIPS TO A PROFESSIONAL FINISH

1.  Heating both A and B resins prior to mixing aids in measuring, mixing, and application of the epoxy finish. Heating thins the two parts and aids in thorough mixing. This heat thinning releases bubbles trapped in the finish during mixing and allows the finish to soak into the wraps more rapidly. Heat the A and B syringes with a lamp, hair dryer, or other heat source until the syringes are no longer cool to the touch, but not hot (about 80 to 90). On warm days this will not be necessary.

1. It is recommended to dispense a minimum of 2cc from each syringe to insure accurate measurement.

1. Bubbles surfacing at the base of guides and trapped under the finish can be popped by gently blowing on the bubbles.

1. Unequal measurement of resin and hardener, incomplete or poor mixing of the two part epoxy may result in an uncured, “sticky” finish. To correct recoat the wraps, taking care to measure and mix thoroughly. A well mixed coat over a slightly sticky finish should cure the problem.

1. Occasionally a frayed end or stick-up of thread may project from a finish. To correct this, allow the finish to dry and then slice off this projection with a sharp knife or razor. Recoat the wrap with Flex Coat Rod Finish.

1. Yellowing of the finish can result from reaction with lacquer-based color preservers, incomplete mixing, or unequal portions of resins A and B.

1. Damaged guides are best removed by shaving or plaining through the Flex Coat finish and thread with a razor knife down to the rod blank. Solvents will not work for cured finish removal.

1. Under certain circumstances (such as when stored in cold areas), epoxy resin part A will crystalize much in same way as honey will crystalize. To restore the resin to its original state, heat the syringe in hot, not boiling water. NOTE: This crystalizing absolutely does not damage Flex Coat Finish.

1. If you do not have a rod support for finishing, cut small “Vs” into the top of a cardboard box to support the rod while finishing.

1. Flex Coat products are available through most rod component suppliers. If you are unable to locate what you need call us for the name of your Flex Coat dealer.

プロフェッショナルな仕上げを実現するための役立つコツ10点は、どれも重要ですが、特記すべきが#4の樹脂が硬化しない場合の原因と修正方法に関するコツ。所定の乾燥時間を過ぎても樹脂が硬化せずにいつまで経ってもベトベトするのは樹脂Aと硬化剤Bが同じ配合比になっていないか、十分に混ぜ合わせていないのが原因。ベトベトの状態がそれほどでもない場合は、正しい配合比（50:50）で十分に混ぜ合わせたコーティング剤を上塗りすれば問題が解決できるそうです。

今回、巻いたスレッドに隙間ができてしまった原因は、スレッドをロッドに巻く時にスレッドにテンションをかける自作の道具を使用せずに、毛鉤製作用のボビンホルダーを使ったことです。ロッドを回転させずに固定してスレッドを巻いたので、下の方にできた隙間に気づかなかったのが原因です。

作業の難易度：5段階で3